Emerging Science Journal

2- Materials and Methods 
2-1- Preparation of PF Resol Resin 
An alkaline catalyst and a molar excess of formaldehyde were used to make resol resins
. 
Resols of varying F: P 
molar ratios were Synthesized, via. 1.5:1, 2:1 and 2.5:1 and designate as R1.5, R2.0 and R2.5 resins respectively. Phenol 
and sodium hydroxide were taken into a two necked round bottomed flask. 0.25 mol% of sodium hydroxide was placed 
on a phenol basis. The two necked RB flask was provided with a mechanical stirrer and a reflux condenser. Whole 
system was kept in a water bath and maintained at 90°C.
Formaldehyde was added at a constant rate with stirring. After the commencement of the reaction a few drops of the 
reaction mixture was taken at regular intervals of five minutes and added to water until permanent turbidity was obtained, 
at that stage the mixture was taken out from the water bath and allowed to cool. Alkaline resin was poured into the 
beaker and neutralized with glacial acetic acid until the pH reached ~ 7.0. The condensate was kept overnight.
2-2- PF Novolac Resins 
An acidic catalyst and a molar excess of phenol to formaldehyde were used to prepare novolac resins
. A 
5 ml of 
glacial acetic acid and 2ml of formaldehyde solution (40%) were and 2g of phenol was added in to it. Beaker was 
wrapped by a cloth. A few ml of concentrated hydrochloric acid was added into the mixture carefully and heated slightly. 
Within five minutes, a large mass of pink plastic was formed. The residue obtain was washed with water, filtered, then 
dried and determined the product yield. Novolac on heating with formaldehyde undergoes cross linking to form infusible 
solid mass called Bakelite. 
2-3- Preparation of Boron Modified Phenol Formaldehyde Resin
Modified resol was prepared at the molar ratio of 1.2 formaldehyde /phenol in the presence of Sodium hydroxide 
catalyst. Setup was placed into round bottomed flask with electrical mechanical stirrer and reflux condenser for 1 hour 
at 70
°
C. followed that boric acid (0.3 mol) was added and heated for 30 min. after that dehydration was performed under 
vacuum at 100
°
C until the total extraction of water. The synthesized resin was cured at 170
o
C in the oven for 1 h. Boron 
modified PF resols were prepared using different amount of boron modifiers as 0.3, 0.5 and 0.8 mol.